AgSn合金粉末非抛物线性内氧化研究.PDF

维普资讯 2006年 6月 贵 金 属 Jun．20o6 第27卷第2期 PreciousMetals 、，01．27．No．2 AgSn合金粉末非抛物线性内氧化研究 江珍雅，陈敬超 (昆明理工大学 云南省新材料制备与加工重点实验室，云南 昆明650093) NonparabolicRateLaw ofInternalOxidationProcessforAgSnAlloyPowders JIANGZhenya，CHENJingchao (KeyLab．ofAdvancedMaterialsofYunnnaProvince，KunmingUniversityof SciencenadTechonology,Kunming，Yunnna 650093，China) Abstract：Usingthemethodofprogressiveoxidationweightgain，thekineticbehaviorofinternal oxidationofAgSnalloy powdersatmoderateand low temperaturerangewasinvestigated．The kineticcurvesofinternaloxidationforAgSnalloypowdersinourstudyarequitedifferentfrom the praaboliclaw showedinWagner’Smode1．Theinternaloxidationmechanismsindifferentstagesofr moderateandlowtemperatureinternaloxidationofAgSnalloypowdersaccordwithdifferentlaws． Thecontrollinkofrkineticbehaviorofinternal oxidationofAgSnalloypowdersatmoderateand lowtemperatureismuturalactionofchemicalreactionanddiffusionofproductlayers． Keywords：Metalmaterials；AgSnalloypowders；Internaloxidation；Nonparabolicratelaw 摘 要：采用逐步氧化增重法，研究了AgSn合金粉末中低温内氧化的动力学行为，结果 表明其内氧化动力学曲线明显不同于高温氧化的抛物线定律，中低温氧化的各个不同阶段 的内氧化机制符合不同的规律，区别于高温氧化，本实验合金粉末的中低温内氧化过程动 力学由化学反应和产物层扩散相互作用控制。 关键词：金属材料；AgSn合金粉末；内氧化；非抛物线定律 中图分类号：TG146．32 文献标识码 ：A 文章编号：1004—0676(2006)02．0022-05 由于 AgMeO中的MeO颗粒细小且均匀分布于Ag基体中，AgMeO系触头材料具有耐电弧烧 蚀、抗熔焊、接触电阻较低等优点，广泛用于中小负荷开关6【J。通过合金内氧化法，在金属基体 中析出均匀弥散的氧化物颗粒将使合金的强度和硬度提高，从而提高合金的耐电弧烧蚀能力和抗熔 焊能力 】【叭。在内氧化过程中，选用较高的温度，则析出的MeO颗粒容易发生粗化f6川，从而影响材 料的机械和物理性能，而在中低温下内氧化，可以很好地控制析出的 MeO颗粒的尺寸。作者采用 AgSn合金粉末作为原料，研究了合金粉末内氧化的动力学行为。 实验方法 以一200目，纯度为99．8％的AgSn合金粉末为原料，其中sn含量为 l4．76wt％，采用逐步氧化增 收稿 日期：2005．09．06 基金项 目：云南省科技攻关(2000B．03)和国家科技攻关(2001BA326C)联合资助项 目。 作者简介：江珍雅．女，在读硕士研究生。目前从事电触头材料研究。 E-mail：leeyaya@tom．tom