TiO2的负载及其对染料废水光降解研究-环境工程专业论文.docxVIP

- - I - 摘 要 以钛酸四正丁酯为钛源，采用溶胶-凝胶法合成 TiO2 溶胶，并以硅藻土和玻璃纤维 网为载体负载 TiO2，制备了负载型光催化剂。以紫外光为光源，一定浓度的酸性大红和 直接大红溶液为目标降解物，研究了悬浮纳米 TiO2 光催化性能及负载型 TiO2 的合成条 件。 研究结果表明：TiO2 对酸性大红和直接大红均具有良好的光催化降解作用，溶液 pH 值、初始浓度、TiO2 投加量、光照时间等参数对降解效果均有一定的影响。在最适 宜条件下酸性大红和的直接大红脱色率分别达 74%和 85%以上。 硅藻土和玻璃纤维网负载后的 TiO2 同样具有良好的光催化降解染料的性能，催化 剂配比、煅烧温度、煅烧时间、玻璃纤维直径等参数对负载型 TiO2 的催化性能均有一 定影响。在最适宜条件下酸性大红和直接大红的脱色率分别达 72%和 66%以上。 关键词：光降解；TiO2；染料；脱色率；负载 - - II - Abstract TiO2 sol was synthesized from 4-butyl titanate by the method of sol-gel and diatomaceous earth and glass fiber net are used for the supported TiO2 to prepared immobilized photocatalysts.a certain concentration of direct red and acid red as solution targeted degradation,Photocatalytic properties of TiO2 suspension and synthesis conditions of supported TiO2 were studied under ultraviolet radiation. The experimental results indicated that: TiO2 have a good photocatalytic degradation for acid red and direct red, the effects of pH, initial concentration,TiO2 dosage, radiation time and other parameters have a certain impact on the degradation effect.the decolorization rate of acid red and direct red reached 74% and 85% in the most suitable conditions. Supported TiO2 by diatomaceous earth and glass fiber network has a good performance of photocatalytic degradation for dyes.the effects of Catalyst ratio,calcination temperature,time of calcination,diameter of glass fiber and other parameters have a certain impact on catalytic performance of supported TiO2. the decolorization rate of acid red and direct red reached 72% and 66% in the most suitable conditions. Key Words：photocatalytic degradation; TiO2;dye;decolorization rate;support 目 录 摘 要 Abstract 1 绪论 1 1.1 光催化技术概论 1 1.2 TiO2 光催化氧化技术的研究发展方向 3 1.3 目前的问题及今后的方向 6 1.4 TiO2 负载方法 7 1.5 负载型 TiO2 的应用 9 1.6 本课题研究目的及其意义 12 1.7 本课题研究内容和方案 12 2 负载型 TiO2 的制备及染料废水的定量表征 14 2.1 光催化剂的制备和模拟染料的配制 14 2.2 负载材料的结构和性质 15 2.3 负载型 TiO2 的制备原理﹑方法 15 2.4 模拟染料的配制 17 2.5 染料废水的分析方法和手段 18 3 TiO2 直接光催化降解染料废水的实验研究 20 3.1 TiO2 直