钙钛矿型LaCoO3纳米管制备方法及性能的研究-化学工程专业论文.docxVIP

摘 要 本论文以钙钛矿 LaCoO3 为切入点，分别考察了不同方法制备钙钛矿型 LaCoO3 纳米管的效果及不同的反应条件对合成 LaCoO3 纳米管的影响，并对获 得的纳米管进行了初步的表征和性能评价，最终得到以下结论： 利用硬模板法可以成功的制备出具有钙钛矿晶型的 LaCoO3 纳米管，而水热 合成法和软模板法无法制备出具有钙钛矿晶型结构的纳米管，其中水热合成法可 以获得 La(OH)3 纳米管； 在采用硬模板法制备 LaCoO3 纳米管的过程中，选取模板的孔径及溶胶粒子 的大小是影响纳米管形成的两个最为重要因素； LaCoO3 纳米管在导电性能方面表现出与颗粒 LaCoO3 相类似的变化趋势，即 LaCoO3 纳米管在低温环境中呈现出半导体的导电性能，当温度升高后，LaCoO3 纳米管的电阻逐渐降低，且 LaCoO3 纳米管电阻降低的幅度要略高于 LaCoO3 颗 粒，在 300℃的时候就可以达到几十Ω，即 LaCoO3 纳米管的导电性能比 LaCoO3 强；在 NO 催化还原实验中，以 LaCoO3 纳米管作为催化剂，NO 在 580℃时出现 最大转化率，转化率达到 45%，比 LaCoO3 颗粒高出 3%左右，而尾气中 CO2 的 含量也比 LaCoO3 颗粒多，多出 0.005%； 导致 LaCoO3 纳米管在 NO 催化还原和导电性能等方面性能有所提升的原因 可能是在形成钙钛矿纳米管的过程中，样品中的活性氧的排布发生变化，在 LaCoO3 纳米管的外表面中活性氧的含量有所增加。 在制备阳极氧化铝模板的过程中，对铝箔的预处理以及降低反应时周围环境 的温度可以提高获得的氧化铝模板的质量，而减小阴阳极板间的距离可以有效的 增大模板的孔径。 关键词： LaCoO3 ，钙钛矿，纳米管，硬模板法，活性氧 ABSTRACT Different methods are investigated for the synthesis of perovskite-type LaCoO3 nanotubes, including its appearance, phase structures and properties. Several conclusions are obtained as follows: We could obtained perovskite-type LaCoO3 nanotubes by the hard template method, and obtained La(OH)3 nanotubes by the hydrothermal synthesis method; The pore size of the templates and the particle diameter are the crucial factor for the synthesis progress of LaCoO3 nanotubes; The electric resistance of the LaCoO3 nanotubes would grow down slightly faster than the LaCoO3 particles as the temperature increased, even decreased to 100Ω at 300℃, thus the electric conductivity of the LaCoO3 nanotubes is better than that of LaCoO3 particles. In the reaction of NO catalytic reduction, the LaCoO3 nanotubes exhibit better catalytic activity than the LaCoO3 particles. The NO conversion rate of it could increase to 45% at 580℃, 2% higher than that of LaCoO3 particles, with the CO2 outlet concentration is 0.005% more simultaneously. We infer that the reason for the better performance of the LaCoO3 nanotubes is attributed as its more active oxygen than LaCoO3 particles. In the process of the preparation of AAO, the pretreat