电化学方法评价缓蚀剂性能的可行性研究应用化学专业论文.docxVIP

英文摘要Subjeet：relating 英文摘要 Subjeet：relating to electrochemistry evaluation of effectiveness of inhibitors Speciality： Name： Instructor： ABSTRACT Weight-loss method iS a classical corrosion research method，but the cycle time of corrosion is too long f．0r oil field application,which’S difficult to adapt the requirements of test of inhibitor application and rapid test of medium corrosion for nle field production units． Wbile electrochemical evaluation is a method，which not only Can rapidly test吨the corrosion rate of a particular time，but also Can study the corrosion mechanism．So electrochemical evaluation method is used in this paper． 曰1e CS300 corrosion tester and CM旧．-45 1 0A corrosion tester have be used to measure the corrosion rate of media in different conditions in this paper,and have be improved appropriately during the experiment．硼1e results indicate that the data of CS300 and CMB--45 1 0A,from the corrosion test in different concen仃鲥。必of NaCl solution．has a poor reproducibility and big error,and Can’t true evaluate the corrosion of mediums，only can judge the corrosion trends of different concentratiOus of NaCl solution；111e reproducibility of date from CⅧ一-45 1 0A is better than CS300 in the corrosive medium of C02 partial pressure；In a l％-2％hydrochloric acid medium,NaCl solution and the solution adding inhibitor of their．the corrosion data has a better reproducibility，Can be applied to judge the corrosion and evaluate the inhibitor in this condition． KeyWords：corrosion，electrochemistry,evaluation method，inhibition efficiency Thesis type：Appfied Research HI 主要符号表主要符号表 主要符号表 主要符号表 物理意义及单位 页码 公式序号 ——极化电流密度，～钿2； 17 2．1 ——极化电流，A； 17 2．1 ——工作电极的表面积，cm?： 17 2-1 ——腐蚀速率，mm]a； 18 2．2 ——腐蚀电流密度，A／cm2： 18 2．2 譬。I＆，圮F ——腐蚀电流密度，A／cm2； 18 2．2 p ——密度，g／cm3； 18 2—2 n ——工作电极材质的失电子数； 18 2．2 VI 学位论文创新性声明本人声明所呈交的学位论文是我个人在导师指导下进行的研究工作及取得的研究成 学位论文创新性声明 本人声明所呈交的学位论文是我个人在导师指导下进行的研究工作及取得的研究成 果。尽我所知，除了文中特别加以标注和致谢中所罗列的内容以外，论文中不包含其他 人已经发表或撰写过的研究成果；也不包含为获得西安石油大学或其它教育机构的学位 或证书而使用过的材料。与我一同工作