介孔SiO2微球的合成及其吸附降解亚甲基蓝的研究化学专业论文.docxVIP

重庆大学硕士学位论文英文摘要 重庆大学硕士学位论文 英文摘要 III III incorporated into the framework or the walls of the silica matrix successfully. Then dye adsorption test was investigated by varying the parameters such as adsorbent dosage and initial concentration of dye. The experimental results indicate that the sample is more efficient for adsorption than pure MSM. When 10 mg of Cu-MSM was added into 15 mg/L of MB concentration, MB removal reached to 95.31%, while 90.55 % to 105 mg/L. Other parameters such as pH, amounts of the sample and initial MB concentration have the same effects to Cu-MSM with MSM. The more amounts of adsorbents, the more dye removal is. Alkaline is favorable to adsorption. Key words: mesoporous silica microsphere (MSM); adsorption; methylene blue 重庆大学硕士学位论文目录 重庆大学硕士学位论文 目 录 PAGE PAGE VI 目 录 中文摘要 I 英文摘要II 1 绪 论 1 1.1 介孔材料的简介 1 1.1.1 介孔材料的定义与特点 1 1.1.2 介孔材料的制备 2 1.1.3 介孔材料的表征 4 1.1.4 介孔材料的分类 8 1.2 介孔材料在吸附中的应用 9 1.3 课题的研究意义及内容 12 1.3.1 课题的学术及应用意义 12 1.3.2 课题的研究内容 14 2 不同结构的介孔二氧化硅微球吸附亚甲基蓝 15 2.1 引言 15 2.2 实验部分 18 2.2.1 试剂及仪器 18 2.2.2 制备方法 20 2.2.3 亚甲基蓝溶液的配制与标定（1.5 g/L） 20 2.2.4 亚甲基蓝标准曲线的绘制 20 2.3 不同结构的介孔二氧化硅微球的表征 21 2.3.1 N2 吸附脱附 21 2.3.2 SEM 23 2.3.3 红外光谱分析 23 2.4 结果与讨论 24 2.4.1 添加量 24 2.4.2 pH 25 2.4.3 吸附时间 25 2.4.4 朗格缪尔等温吸附方程 26 2.5 本章小结 27 3 介孔 SiO2 微球负载 TiO2 吸附亚甲基蓝 28 3.1 引言 28 3.2 实验部分 30 3.2.1 试剂及仪器 30 3.2.2 制备方法 31 HYPERLINK \l _TOC_250002 3.3 介孔 SiO2 微球负载 TiO2 的表征 31 HYPERLINK \l _TOC_250001 3.3.1 XRD 31 3.3.2 N2 吸附脱附 32 HYPERLINK \l _TOC_250000 3.3.3 SEM 33 3.3.4 红外光谱分析 34 3.4 结果与讨论 34 3.4.1 添加量 34 3.4.2 pH 35 3.4.3 温度 36 3.4.4 紫外光照与可见光照 36 3.4.5 吸附等温线 38 3.4.6 吸附动力学 39 3.5 结果与讨论 40 4 Cu 修饰的介孔二氧化硅微球吸附亚甲基蓝 41 4.1 引言 41 4.2 实验部分 42 4.2.1 试剂及仪器 42 4.2.2 制备方法 43 4.3 Cu-MSM 的表征 43 4.3.1 XRD 43 4.3.2 N2 吸附脱附 44 4.3.3 SEM 44 4.3.4 红外光谱分析 45 4.3.5 原子吸收光谱法（AAS） 45 4.4 结果与讨论 46 4.4.1 添加量 46 4.4.2 时间 46 4.4.3 浓度 47 4.5 本章小结 48 5 结论与展望 49 5.1 结论 49 VII VII 5.2 展望 49 致 谢 51 参考文献 52 附 录 56 A 作者在攻读学位期间发表的论文目