c692-97中文版-评估奥氏体不锈钢的外应力腐蚀断裂趋势对绝热材料的影响的标准试验方法.docVIP

C 692 PAGE 661 Designation: C 692 - 97编号：C692-97 PAGE 646 Standard Test Method forEvaluating the Influence of Thermal Insulations on ExternalStress Corrosion Cracking Tendency of Austenitic StainlessSteel This test method is under the jurisdiction of ASTM Committee C-16 on Thermal Insulation and is the direct responsibility of Subcommittee C16.31 on Chemical and Physical Properties.本试验方法由ASTM委员会C-16绝热委员会管辖，并由C16.31化学和物理性能分委会直接负责。Current edition approved Nov. 10, 1997. Published June 1998. Originally published as C 692 - 71. Last previous edition C 692 - 95a.现行版本于1997年11月10日批准，并于1998年6月出版。最初版本编号为C692-71。上一版本编号为C692-95a。 This test method is under the jurisdiction of ASTM Committee C-16 on Thermal Insulation and is the direct responsibility of Subcommittee C16.31 on Chemical and Physical Properties.本试验方法由ASTM委员会C-16绝热委员会管辖，并由C16.31化学和物理性能分委会直接负责。Current edition approved Nov. 10, 1997. Published June 1998. Originally published as C 692 - 71. Last previous edition C 692 - 95a.现行版本于1997年11月10日批准，并于1998年6月出版。最初版本编号为C692-71。上一版本编号为C692-95a。 This standard is issued under the fixed designation C 692; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (ε) indicates an editorial change since the last revision or reapproval.本标准以固定编号C692刊发；紧随编号后的数字表示最初采用的年份，或者是修订版的最后修订年份。圆括号中的数字表示最新重新批准的年份。上标(ε)表示自上一修订版或重新批准后的编辑性修改。 1. Scope适用范围 This test method covers two procedures for the laboratory evaluation of thermal insulation materials that may actively contribute to external stress corrosion cracking (ESCC) of austenitic stainless steel due to soluble chlorides within the insulation. It should be understood that this laboratory procedure is not intended to cover all of the possible field conditions that might contribute to ESCC.本试验方法包括对绝热材料实验评估的两种程序。由于绝热材料中可溶性氯化物的存在，这种材料可对奥氏体不锈钢的外应力腐蚀断裂起到积极作用