编号123 表4 混凝土组成及性能 混凝土的组成/(kg/m 3标养28d 抗折强度/MPa 6.945.435.74 W/C 0.30.40.5 水泥 550450400 水 165180200 碎石 100010501050 砂 750780800标养28d 抗压强度/MPa 70.4957.4850.73 2007年第9期(总第215期 Number 9in 2007 (Total No.215混凝土 Concrete 董必钦,罗 帅,邢 锋 (深圳大学土木工程系,深圳市土木工程耐久性重点试验室,广东深圳518060 Abstract:Effects of sulfate attack on different sorts of concrete in sulfate solution/under drying and wetting cycles/under flexural load or the combine of them were studied ,the corrosions reason of sulfate attack were investigated by analyzing the corrosion product with XRD.Results show the corrosion mechanisms of sulfate attack due to single damage factor and multiple damage factors were not all the same ,and multiple dam-age factors could indicate the concrete structure due to sulfate attack more exactly.Key w ords: concrete ;sulfate attack ;drying wetting cycles ;single damage factor ;multiple damage factors 摘要: 研究了不同水灰比配制的混凝土在浸泡/干湿循环/弯曲荷载及其复合作用下的 硫酸盐侵蚀规律;并用XRD 等微观方法对侵 蚀机理进行了表征。结果表明:混凝土在单一破坏因素作用下侵蚀规律与多因素 共同作用下的侵蚀规律并不相同,多因素侵蚀作用的规律能更准确地反映实际工程 中的侵蚀规律。关键词: 混凝土;硫酸盐腐蚀;干湿循环;单一破坏因素;多重破坏因素 中图分类号: TU528.01文献标志 :A 文章编号:1002-3550-(200709-0033-04 Study on sulfate corrosion of concrete under m ultiple dam age factors DONG Bi-qin ,LUO Shuai ,XING Feng (The Key Lab on Durability of Civil Engineering in Shenzhen ,Department of Civil Engineering ,Shenzhen University ,Shenzhen 518060,China 多因素作用对混凝土硫酸盐腐蚀的影响研究 收稿日期:2007-03-14 基金项目:国家自然科学基金资助项目广东省自然科学基金资助项目 0引言 对于混凝土的硫酸盐腐蚀,人们关注的常常是在试验室按 照现有标准测得的抗压强度、抗折强度和硫酸盐浸泡时间等单一破坏因素 (single damage factor ,SDF 作用下的耐久性指标。然而,在实际工程中,结构混凝土的耐久性 问题是一种在荷载 作用下的干湿循环、荷载等多种破坏因素交互作用的复杂问题。如何考虑实际工程 中复杂的双重破坏因素(double damage factors ,DDF 或多重破坏因素 (multiple damage factors ,MDF 特点,运用在试验室得到的试验结果能客观地反映结构工程中混凝土的耐久性或者 使用寿命,是当前混凝土科学的一个重要研究课题[1] 。20世纪90年代以来,关于混凝土在 (弯曲荷载+Na 2SO 4腐蚀[2]DDF 和 (冻融+Na 2SO 4腐蚀[