中高含硅钢抑制“圣德林效应”的研究.pdfVIP

The 6th China Corrosion Conference Research on Inhibiting the “Sandelin Effect” of Medium to High Silicon Steel Fujun LI, Shiqiang GUO, Dong SUN, Jianqiang YAN North Petroleum Venture Technology Co. LTD, Daqing, Heilongjiang, China, 163316 Abstract: Medium to high silicon steel would produce sandelin effect in the process of hot dip plating, result in bad binding force and easy peeling off of the coating. Repeated experiments show that special polybasic alloy added to zinc bath with oscillator in the process of hot dip plating, can inhibit the sandelin effect availably. At the same time, it can repair corrosion defects in the tubing surface through alloying. Keywords: High silicon steel; Sandelin effect; Alloyin 中高含硅钢抑制“圣德林效应”的研究 李福军，郭士强，孙东，严建强 大庆高新区北油创业科技有限公司，黑龙江，大庆，中华人民共和国，163316 摘 要：油田油管属中高含硅钢管，在热浸镀过程中通常产生“圣德林效应”，致使镀层结合力差， 易起皮脱落。多次实验表明，向锌浴中添加专用多元合金及热浸镀过程中振荡器的使用可有效抑制“圣 德林效应”（Sandelin effect ）的产生，同时还可以使油管表面腐蚀缺陷通过合金化得以修复。 关键词：高硅钢；圣德林效应；合金化 1 前言 硅，或有时硅加铝。因此，在结构件热浸镀锌中，通常 会遇到高反应强度的钢材。早在 20 世纪 40 年代，圣德 油田油水井中普遍存在管材腐蚀问题，通常 10 年 林就研究过 Si 对于热浸镀锌层组织的影响，他指出： 寿命的管材,在腐蚀严重的油气田中半年就腐蚀穿孔。特 在正常的镀锌温度范围内（通常为 450 ℃左右），钢基 别是大庆油田已进入高含水开发后期，为了保持石油量 体中含 Si 量在 0.1%左右和大于 0.3%时，对镀层的影响 的高产稳产，聚合物驱及三元驱已开始大面积应用，油 最大，人们称之为“圣德林效应。 水井油管及地面管道腐蚀与结垢逐年加重，导致油水井 不能正常生产，造成很大经济损失，同时严重污染环境。 3 添加多元合金抑制圣德林效应 针对这一现状，本文研究了一种集“材料保护+隔离保 3.1 实验工艺流程及参数 护+ 电化学保护+废旧管微裂纹修复”四位一体的油管及 本实验采用溶剂法热浸锌工艺，即将经过前处理的 地面管道防腐的新方法，通过添加稀土多元合金，解决