HDPE薄膜低温等离子体改性与粘接性能研究.pdfVIP

6 PACKAGING ENGINEERING Vol. 31 No. 112010. 06 HDPE薄膜低温等离子体改性与粘接性能研究 1, 2 1 解林坤 , 李树材 ( 1., 300222; 2. , 650224) : 利用氧气低温等离子体, 在真空度为20 Pa, 处理功率为30 W 的条件下, 对高 度聚乙烯( H PE) 薄膜 进行了表面改性研究结果表明:在 20~ 200 s 的处理时间内, 单位面积的失重率随处理时间的增加线性增 大,表面粗糙度也随着增加; 处理后薄膜表面的接触角显著减小;接触角越小, 剥离强度就越大; 处理后能在薄 膜表面形成羟基羰基和羧基等各种极性基团 : 低温等离子体; 高 度聚乙烯; 接触角; 剥离强度 : TB484. 3; TB487 : A : 1001- 3563( 2010) 11- 0006- 04 Research on Modification andAdhesiveProperty for Low TemperaturePlasma of HDPE(Highdensity Polyethylene) ilm X I E L ink un 1, 2 , L I S hucai 1 ( 1.Tianjin University of Science T echnology, Tianjin 300222, China; 2. Southwest Forestry College, Kun ming 650224, China) Abstract: Modify the thin film of H PE ( High ensity Polyethylene) by using low temperature plasma of oxy gen at 20 Pa of vacuum and 30 W of processing power. The results show that: between 20~ 200 s, the weight loss rate per area unit and surface roughness increase with the processing time; T he contact angles of the film surface reduce dramatically after processing; the smaller the contact angle is, the greater the peel strength will be; the thin film surfacewill form some polar species such as hydroxyl, carbonyl and carboxyl after processing. Key words: low temperature plasma; H PE; contact angle; peel strength ( H PE) , , , H PE [ 1] , , FTIRAT R SEM [2- 3] ;, AFM , , H PE [4- 6] , 1 () [7] 1. 1 , 3 H PE (0. 08 mm, 0. 951 g/ cm ) , , , 50 mm 50 mm 30 mm 120 mm , , , 15 min,, : : ( 209306) ;(500929) : ( 1974- ) , , ,,,