浅谈梅钢冷轧厂连退机组7号CPC+跑偏及处理.pdfVIP

浅谈梅钢冷轧厂连退机组 7 号 CPC 跑偏及处理1 俞永胜 何志祥 胡建农 欧阳智勇 （宝钢集团上海梅山钢铁公司设备部，南京 210039 ） 摘 要 本文针对冷轧厂连退机组钢带在 SF 段的跑偏及在 SF 段炉子距离较长、带钢在温度高时，带钢延伸率变 化大、容易发生带钢与炉辊打滑、跑偏的现象；进行了逐步分析并再处理，使连退机组由原来的 0.2mm 厚度以下 的带钢保持在 450mpm 速度上稳定运行提升到 600～630mpm 速度稳定运行的同时，为下一步机组再次提速积累 了经验。 关键词 CPC 带钢跑偏 辊子 Research on the Strip Misalignment in 7# CPC of CAL in Meishan Cold Rolling Mill Yu Yongsheng He Zhixiang Hu Jiannong Ouyang Zhiyong (Equipment Department of Baosteel Meishan Iron Steel Co., Ltd., Nanjing, 210039) Abstract This paper discussed the phenomenon including the strip misalignment in 7# CPC and the strip skid on the rollers in CAL . The influence factors cover the length of SF section , the temperature of the strip and so on. Solutions were put forward by analysis of the factors above , and were put into practice successfully. The steady speed of the strip ( the thickness under 0.2mm ) was prompted from 450 mpm up to 600 mpm — 630 mpm , and meanwhile experience was prepared for the next prompt of the speed in CAL. Key words CPC, the slip misalignment, the strip skid 1 引言 梅钢冷轧厂连退机组热试以来，在生产 0.25ｍｍ厚度以下带钢时，工艺段速度超过350mpm 以上时炉 内7 号CPC 处带钢出现严重的跑偏现象，此问题一直制约着整个机组热调试项目的展开和机组的提速生产， 严重影响了连退机组产能发挥。难以满足机组工艺技术要求及充分发挥连退机组的产能。 2 7 号 CPC 跑偏原因分析及问题查找 7 号 CPC 处带钢出现严重的跑偏一般有两个方面的主要原因。CPC 装置本身纠偏性能不佳,无法起到 纠偏作用:系统辊系安装精度差产生严重跑偏，超过 CPC 装置的纠偏性能力。 2.1 7 号 CPC 跑偏原因的查找 （1）带钢跑偏。带钢在运行中自行偏离生产线的中心，向辊子的一边移动，称为“带钢跑偏”。带钢 在输送辊上运行，只要带钢和辊子表面有接触，并在一定的磨擦阻力界限内，那么带钢上各点就会和辊子 俞永胜，男，大专，工程师，从事冶金设备检修管理，yuyongsheng8888@126.com 8-186 第八届（2011 ）中国钢铁年会论文集 的中心线成直角行走。假设带钢板形良好，断面厚薄均匀，则作用在带钢上的张力分布均匀，同时各辊子 保持平行，并与带钢运行方向保持垂直，那么，带钢在辊子上运行就不会跑偏，即带钢时刻运行在生产线 的中心上。CPC 是对中纠偏即保证带钢的中心始终在机组中心线上，当带钢跑偏时，它是通过纠偏辊使跑 偏的带钢在摩擦力的作用下回到机组中心来完成纠偏任务的。 但在实际的生产过程中，会有各种各样的因素影响带钢的正常运行轨迹，因此使带钢产生跑偏现象。 经过对 7#CPC 相关安装基准尺寸复核均在