PAGE  PAGE 5 氟化铝流化床反应器的制造 　　摘要：氟化铝（AlF3）流化床反应器是干法生产氟化铝的核心设备，目前，氟化铝流化床反应器一般由304不锈钢制成，在低速冲刷条件下抗点蚀和抗应力腐蚀性能能力较差，而且在高温条件下易出现氧化反应。而Inconel 600镍基合金具有良好的耐高温腐蚀和抗氧化性能、优良的冷热加工和焊接性能。本文介绍了Inconel 600材料特性、焊接要点、流化床部件成型、总装等。 　　Abstract： The aluminum fluoride （ALF3） fluid-bed reactor is the core equipment of dry process aluminum fluoride. At present， aluminum fluoride fluid-bed reactor is generally made from 304 stainless steel， with poor abilities of resistance to pitting corrosion and stress corrosion resistance under the condition of low velocity， and under high temperature conditions， the oxidation reaction is easy to occur. And Inconel 600 Ni base alloy has good resistance to high temperature corrosion and oxidation resistance， excellent cold and hot processing and welding performance. This paper introduces the Inconel 600 material properties， welding points， fluid-bed parts molding and assembly etc. 　　关键词：氟化铝；流化床；制造 　　Key words： aluminum fluoride；fluid-bed；manufacture 　　中图分类号：TG457.1 文献标识码：A 文章编号：1006-4311（2016）18-0112-02 　　0 引言 　　氟化铝流化床反应器是干法生产氟化铝工艺过程中的核心设备，设计压力是负压-0.05MPa，使用温度高达630℃。氟化氢气体和AL（HO）3粉末在床层上相遇发生化学反应，生成氟化铝。氟化铝（AlF3）是铝电解生产过程中的一种主要辅助材料，是铝电解的助熔剂。 　　目前，氟化铝流化床反应器一般由304不锈钢制成，在低速冲刷条件下抗点蚀和抗应力腐蚀性能能力较差，而且在高温条件下易出现氧化反应。而Inconel 600镍基合金具有良好的耐高温腐蚀和抗氧化性能、优良的冷热加工和焊接性能，在630℃下具有满意的热强性和高的塑性。因此，选用Inconel 600镍基合金作为氟化铝流化床反应器的材料。 　　Inconel 600镍基合金化学成分和力学性能见表1和表2。 　　1 结构 　　流化床反应器为立式容器，在其内部设有上下两个床层，AL（HO）3以环境温度由顶床给料螺旋加入顶部床层，HF气体从底部进入底部床层，在床层上进行化学反应生成氟化铝（AlF3）。 　　2 工艺流程 　　2.1 工艺组成 　　制定科学合理的制造工艺，根据板料实际板幅绘制合理的壳体排板图（合理确定焊缝布置，焊缝避开开孔、床层位置等），编制产品制造检验大纲，实施和控制产品制造全过程。 　　2.2 下料 　　严格按排板图要求划线，Inconel600材料不得打样冲眼，壳体件直线部分采用剪切下料，坡口采用机械方法加工并去毛刺飞边，非直线部分采用等离子切割下料并打磨见金属光泽。在制造过程中必须严格保护好板面，应将剪床、刨边机等设备台面覆以胶皮、毛毡、纸板等物，卷板机卷辊为不锈钢辊。工作台面衬不锈钢板，并要平整无焊疤。镍合金板不得直接接触地面，以避免磕碰划伤。设备吊装用吊装带。 　　2.3 筒体 　　根据Inconel600板材实际板幅绘制筒体排板图，确保开孔、床层、加强圈等避开焊缝，筒节间纵缝及与锥形封头拼缝错开至少100mm以上。筒节展开长度应等于锥形封头大端中径展开长度。严格控制下料尺寸公差，要求其边长允差为±1.5mm，对角线允差为≤2mm。 　　筒节卷制后，纵缝两端必须对齐，对口错边量≤1.0mm。焊后找圆，筒体最大最小直径差符合图样及标准要求，焊缝棱角度≤2.8mm。 　　2.4 顶