冻裂钢管柱初步有限元研究.docVIP

冻裂钢管柱初步有限元研究摘要:本文介绍了某位于北方的工程，大量采用的焊接钢管柱在气温突然降至零下20℃左右时，有小部分钢管柱出现很明显的裂缝。后经查验表明钢管内存在大量积水，本文采用有限元软件模拟水结冰后体积膨胀对钢管的附加应力分布，来初步验证是否是水结冰体积膨胀导致钢管胀裂。 关键词:焊接钢管柱，开裂 ， 胀裂 Abstract: this paper introduces a located in the north of the project, the welding steel tube column used in great quantities in the temperature suddenly dropped to about 20 ℃ below zero, a small group of steel tube column appears very obvious cracks. After inspection showed that there are lots of water inside pipe is adopted in this paper, the finite element software to simulate the icy water volume of steel tube inflation after additional stress distribution, to preliminary validation is icy water volume expansion contributes to steel tube distends to crack. Keywords: welding steel tube column, craze, distends to crack 中图分类号：TU74文献标识码：A 文章编号： 一、前言 钢管混凝土结构由于充分发挥了混凝土与钢材的材料特性，具有承载力高、塑性与韧性好、节省材料等显著特点，同时钢管混凝土结构一般外形规则，梁柱连接相对简单，结构设计与施工都较方便，是一种综合性能优良的新型组合结构，在实际高层建筑工程中得到了广泛的应用并取得了较好的技术经济效益。柱形钢管混凝土结构是钢管混凝土结构中应用较多的一种，目前我国对柱形钢管混凝土的研究主要集中于单一构件受力性能及设计方法的研究，而对有限元的研究相对较少，而在钢结构设计中，设计的好坏也是结构安全与否的关键因素之一。现有的方形钢管混凝土柱与H型钢梁的连接主要有刚接与铰接两种节点类型，对方形钢管混凝土梁柱半刚性连接的研究并不多见。相关文献对方钢管混凝土柱与钢梁上下顶底角钢半刚性连接节点做了试验研究及有限元分析，宗周红等通过拟静力试验研究了矩形钢管混凝土柱与钢梁两种半刚性节点—加劲端板连接与双T板连接节点的抗震性能。为此，本文参照相关文献，结合某位于北方的工程钢结构冻裂情况，采用有限元软件模拟水结冰后体积膨胀对钢管的附加应力分布，来初步验证是否是水结冰体积膨胀导致钢管胀裂。 二、工程概述 某工程位于北方，工程中大量采用直径1000mm，壁厚50mm的焊接钢管柱，钢材强度为Q345C。在气温陡然降至零下20℃左右时，小部分钢管柱出现很明显的裂缝，后经加热后钻孔查验表明，这些钢管中存在大量的积水。猜想钢管中积水在降温结冰后体积膨胀导致钢管胀裂，因此本文采用有限元软件模拟水结冰后体积膨胀对钢管的附加应力分布，来初步验证是否是水结冰体积膨胀导致钢管胀裂。 三、分析模型及参数 （一）材料力学参数： Q345钢：弹性模量E=206GPa，泊松比ν=0.3，线膨胀系数α=1.2X10-5。 冰：采用固体单元升温时的体积膨胀来模拟水变成冰时的体积膨胀。模拟冰的固体单元的弹性模量E=5GPa，泊松比ν=0.3，假定线膨胀系数α=3.228X10-2（保证在升温1摄氏度条件下体积能够膨胀10%，以模拟水变成冰时的体积膨胀）。 （二）分析软件与模拟单元： 采用Midas-Gen作为分析的软件。考虑到水结成冰时体积是想各个方向同时膨胀的，因此无论是钢管还是冰都采用实体单元模拟。 （三）有限元模型： 由于所有钢管柱的长度不一样，因此没有建立一根完整的钢管柱模型，而是取其从其顶面向下延伸约2.0m的一段。所建立的有限元软件如下图所示： 用于分析的整体有限元模型 内部的冰 所截取的钢管柱 钢管柱顶部的盖板和十字加劲肋 （四）边界条件： 由于是截取钢管柱一部分所做的有限元模型，因此其边界条件只是在模型底面约束了Z向变形，X，Y没有约束。 （五）荷载施加与分析方法：