提高转炉 10 号、20 号钢顶锻完好率 ·1 · 提高转炉 10 号、20 号钢顶锻完好率 秦 义 （杭州钢铁集团公司转炉炼钢厂, 杭州 310022 ） 摘 要 本文主要介绍了杭钢转炉厂冶炼 10 号、20 号钢的生产工艺实践，对以上钢种在顶锻检测过程中发现的表 面纵向裂纹缺陷进行了总结及分析，针对产生原因采取了控制精炼钢水氮含量和钙含量，及提高精炼要钢温度符合 率和中包温度符合率等措施，使得铸坯脆性降低、浇注过程中的拉速和液面波动稳定，从而减少了 10 号、20 号钢 的改判次炉数，提高了顶锻完好率，满足了用户的加工要求。 关键词 氮含量 钙含量 中包温度 拉速 结晶器液面波动 Improve the Intact Rate Upsetting of the 10# and 20# Steel Qin Yi (The Converter Steelmaking Plant of Hangzhou Iron and Steel Group Company, Hangzhou, 310022) Abstract This article introduces the production technology of 10#、20# in convertor factory ,iron and steel company of Hangzhou. The defection of furnace longitudinal crack through upsetting tests was founded and analyzed. Besides controlling the nitrogen and the calcium contents of refining steel, measures of raising the coincidence of tundish temperature were used to reduce the fragility of casting and stabilize the pulling rate and fluctuation of crystallizer liquid level, further reduce the number of commuting of 10#、20#. The intact rate of upsetting was finally improved to satisfy the processing demands. Key words nitrogen content, calcium content, tundish temperature, pulling rate, fluctuation of crystallizer liquid level 1 前言 转炉全质办在近年来协助公司售后服务科处理异议过程中发现，随着 10 号、20 号在汽车车身、手刹蹄 片、杠杆轴、变速箱速叉、传动被动齿轮等中的广泛使用和汽车从卖方市场转变为买方市场，用户在激烈的 竞争环境下对杭钢的 10 号、20 号的质量要求越来越高，特别是表面质量，稍有缺陷就会造成产品的报废， 不仅浪费了加工成本还给用户带来了不可估量的信誉损失。在这个现状下集团公司对转炉生产的 10 号、20 号钢也提出了很高的要求，只要顶锻发生裂 1、气 1 就改判为普碳钢，如果发生裂 3 和气 3 就有可能判次废， 再加上异议赔款给转炉造成了很大的损失。本文结合转炉厂的生产实际，对 10 号、20 号钢表面纵向裂纹的 产生原因进行了分析，并提出改进措施。 2 原因分析 2.1 缺陷特征 针对近期发生的 10 号、20 号顶锻缺陷（图 1），我们组织专人对轧材进行抽样，同时对抽检样进行酸洗 秦义，男，本科，工程师，从事质量管理，qinyi@ ·2 · 第九届中国钢铁年会论文集