TiB2复合化学镀光亮镍磷合金-化学工程专业论文.docxVIP

西南科技大学硕士研究生学位论文第 西南科技大学硕士研究生学位论文 第 PAGE 2 页 Abstract The main content of this paper is electroless composite plating of brightening nickel with TiB2. At present, TiB2 is normally used in ceramic materials，and it is not widely used in the field of plating.A special coat that evenly mixes one or several infusible solide grains to the electroplating coating is called composite coating.If we can use TiB2 to electroless plating,we can make the gain distributing well- proportioned,the coating finely.Thus the aim of this paper is to do experiments to find surfactant、brightener and portfolio agent whether it is possible to compositely plate brightening nickel with TiB2, especially in the manner of electroless plating. The aim of the experiment is determined electroless plating solution formula 、surfactant、brightener and temperature、PH.Research work to the compound coating organizational structure and the coating performance. Key words: TiB2 composite plating;electroless plating;brightening nickel plating 目 录 1 绪论 1 1.1 化学镀的发展与现状 1 1.1.1 化学镀工艺 1 1.1.2 化学镀原理 5 1.1.3 各组分的作用 7 1.2 课题概况及研究意义 9 1.3 课题的研究内容及目的 12 1.4 课题主要技术要求以及制定的方案 12 2 实验部分 14 2.1 工艺研究方法 14 2.2 实验流程 14 2.3 处理工艺步骤 14 2.3.1 样板打磨 14 2.3.2 化学除油 14 2.3.3 酸洗除锈 15 2.3.4 活化 15 2.3.5 TiB2 的前处理 16 2.3.6 酸性化学镀光亮镍 16 2.3.7 实验药品 17 2.4 性能测定的方法 17 3 TiB2 复合化学镀光亮镍磷合金的工艺研究 19 3.1 各组分的选用 19 3.2 复合化学镀光亮镍磷合金的结果与讨论 29 3.2.1 pH 值的影响 28 3.2.2 温度的影响 30 3.2.3 TiB2 添加量的影响 31 3.2.4 搅拌速率的影响 32 3.2.5 镀液中负载因子的影响 32 3.2.6 表面活性剂的影响 33 3.2.7 光亮剂的影响 33 3.2.8 络合剂的影响 33 3.2.9 镀层性能的研究 34 结 论 52 致 谢 54 主 要 参 考 文 献 56 附 录 59 攻读硕士学位论文期间发表的学术论文及研究成果 60 西南科技大学硕士研究生学位论文第 西南科技大学硕士研究生学位论文 第 PAGE 10 页 1 绪论 1.1 化学镀的发展与现状 化学镀工艺 化学镀的发展史中最重要便是化学镀镍的发展史。Wurtz意识到水溶液中 磷回收镍，但化学镀镍的创始人是美国国家标准局的特殊技能的A.Brenner和 G.Ridell。他们建议在1947无镍粉的方式沉积，明确包括涂层的催化特性，无 电解镀镍技术产业有可能的操纵。因此，历史上的无电镀镍工艺是很短的，真 正有规模的行业或70年代后期的事。最初的5%－8%（重量）只要在磷镀层的磷， 磷80在早期增长9% - 12%