You need to determine beforehand whether you are dealing with a major or minor repair. In the case of deep scratches, you have to level the damage using a special 2K putty. After drying and sanding the surface, you prepare the next steps which are the same as for minor repairs. Thoroughly clean the puttied and sanded area. By matting around the sanded area you ensure that the transition from the repaired area to the old paintwork is not visible after polishing. --- --- It is absolutely essential to follow the recommendations of the manufacturers of IR dryers. Overheating plastics may lead to a deformation of the add-on part which in some cases are irreversible. --- Since plastics were first introduced, Spies Hecker deals with the question of how to refinish these substrates. It developed a series of special products in order to meet the special requirements of the different types of plastic. Thus, next to its renowned surfacers and top coats for vehicle refinishing, Spies Hecker offers special additional products for painting plastics. --- --- --- --- --- --- --- 适用范围 : 柔软添加剂用于2K中浓度和高浓度漆料中 (面漆, 清漆和2K中间漆). 混合比例 : 面漆, 清漆和中间漆都必须添加30%. 然后以2:1比例添加硬化剂. 如果2K中间漆使用了柔软添加剂, 则必须以2:1的比例添 加硬化剂. 特别提示 : 我们不建议将中间漆8590/5030与柔软添加剂混合后, 作 长时间的储存 为了得到最佳的打磨性, 需将漆面于60°C下干燥45分钟 保美耐柔软添加剂9050. 第二十八页，共四十六页。 保美耐纹理效果添加剂 SA 101 粗纹, SA 102 幼纹.  使用范围 : 一种系列适用于中浓度和高浓度面漆系列. 混合比例 : 以1:1 的体积比混合保美耐270高浓度面漆系列 再以 3:1 的体积比混合保美耐硬化剂. 以0.8:1 的体积比混合保美冠257面漆系列. 再以 2:1 的体积比混合保美冠硬化剂 使用限期 : 3小时 第二十九页，共四十六页。 保美耐哑光添加剂 MA 100. 使用范围 : 一种哑光剂适用于高浓度和中浓度面漆系列. 混合比例 : 以 1:1 的体积比混合保美耐高浓度270面漆系列. 再以 3:1 的体积比混合保美耐硬化剂. 以 0.8:1 的体积比混合保美冠257面漆系列. 再以 2:1 的体积比混合保美冠硬化剂.  特别提示 : 不适合用于清漆系列之内. (可使用保美冠 8070 / 8085 哑光清漆代替). 第三十页，共四十六页。 适用范围 : 绸缎光泽的中浓度清漆 混合比例 : 以 2:1 的比例混合中浓度硬化剂 喷涂层数 : 2 层 特别提示 : 此清漆具有柔软性. 保美冠柔软清漆 8070 绸缎光泽. 第三十一页，共四十六页。 适用范围 : 高光泽的中浓度清漆漆面 混合比例 : 以 2