不同制备方法对Cd0.1Cu0.01Zn0.89S光催化剂产氢性能影响的研究.pdfVIP

不同制备方法对Cd0.1Cu0.01Zn0.89S 光催化剂 产氢性能影响的研究 ∗ 刘冠杰，郭烈锦 西安交通大学动力工程多相流国家重点实验室，西安，710049 摘要：本文通过不同的制备方法合成了Cd0.1Cu0.01Zn0.89S 新型光催化剂，并通过XRD,SEM 和UV-vis 吸收光谱对催化剂进行了表征。对比发现，高温合成的催化剂产氢能力反而下降。 共沉淀法合成的催化剂具有最高的产氢活性，无负载时在可见光照射下产氢速率为 350μmol/h 。 关键词：光催化剂；可见光；氢气 中图分类号：TQ426.62 文献标识码：A Study on photocatalytic activity for hydrogen evolution over Cd0.1Cu0.01Zn0.89S catalysts by different synthesis methods Guanjie Liu, Liejin Guo* State Key Laboratory of Multiphase Flow in Power Engineering, Xi’an Jiaotong University, Xi’an, 710049 Abstract: Cd Cu Zn S photocatalysts were prepared by different methods, and characterized x y 1-x-y by XRD, SEM and UV-vis spectra. Compared with each other, it was found that the photoactivity decreased when the temperature in the preparing process increased. The photocatalyst prepared by coprecipitation method had the highest photoactivity. The rate of hydrogen production without any cocatalysts is 350μmol/h under visible light irradiation. Key words: photocatalyst; visible light; hydrogen 引言 光催化分解水制氢被认为是有望解决世界范围内的能源和污染问题的途径，但是目前已 有的光催化剂大多数只能在紫外光照射下分解水[1,2]，而太阳能主要集中在可见光部分，要 有效利用太阳能必须发展对可见光有响应的光催化剂。令人遗憾的是目前能够在可见光照射 下分解水的催化剂依然很少[3,4]。 要实现光催化剂对可见光的响应，一个最基本的条件就是要有较窄的禁带。实现这一 目标一般通过对宽禁带的光催化剂进行掺杂或合成固溶体来实现。催化剂掺杂较为典型的有 973 计划（No.2003CB214500 ）和国家自然科学基金（No.）资助课题 ∗通讯联系人，lj-guo@mail.xjtu.edu.cn. Ni 、Ta 共掺杂TiO [5]，Cu、Ni 掺杂ZnS[6,7] ；同时固溶体合成光催化剂的方法越来越受到 2 关注，而且取得了很大的进展，比如：ZnS-CdS[8,9,10] ，AgInS2-ZnS[11]，CuInS-ZnS[12]， AgInS -CuInS -ZnS[13]和GaN-ZnO[14] 。 2 2 ZnS 由于其高的导带，在不负载Pt 等贵金属的情况下仍然拥有很高的产氢活性，但其 光响应范围仅仅局限在紫外区[15]。以ZnS 为主材料进行掺杂或合成固溶体都取得了很好的 效果[6-13]。其中对ZnS-CdS 的研究较为全面, CdS 在不负载Pt 的情况下产氢能力较弱，而 如上所述，ZnS 没有可见光响应。二者的固溶体可以较好的解决这些问