化学通报 2001 年 第64 卷 w 109 碳纳米管制备温度对其嵌锂性能的影响 吴国涛 陈茂惠 朱光明 尤金跨 林祖赓* 厦门大学化学系 固体表面物理化学国家重点实验室 厦门 361005 摘 要 本文利用 XRD 和 RAMAN 等方法对甲烷在 500~700 范围催化裂解制备的碳纳米管 结构进行了表征 同时考察了其电化学嵌锂性能 结果表明碳纳米管的制备温度对其锂嵌入脱出电 位 可逆容量和充放电循环性能均有显著的影响 并且其嵌锂机理类似于低温热解碳(低于1000 ) 关键词 碳纳米管 催化裂解 甲烷 锂离子电池 Effects of Preparation Temperatures on Lithium Insertion Properties of Carbon Nanotubes WU Guotao, CHEN Maohui, ZHU Guangming, YOU Jinkua, LIN Zugeng (Dept. of Chemistry State Key Lab. for Physical Chemistry of Solid Surface, Xiamen Univ., Xiamen 361005) Abstract In the present work, carbon nanotubes were produced by catalytic decomposition of methane at low temperature range (500~700 ) on Ni-catalysts. Structures and lithium insertion properties of these carbon nanotubes were characterized by X-ray diffraction (XRD), Raman spectroscopy and electrochemical measurements, respectively. The results showed that preparation temperatures of carbon nanotubes have remarkable effects on both specific capacity and cycle life. The mechanism of lithium insertion into carbon nanotubes is similar to that of carbon produced by the pyrolysis of hydrocarbon below 1000 . Key words Carbon nanotube, Catalytic decomposition, Methane, Lithium ion batteries 锂离子电池是近年发展起来的一种新型电池, 它的正极采用高电位的过渡金属氧化物,负极 大多采用具有特殊结构的碳材料, 通过锂离子在两极的嵌入和脱出来贮存和释放电能 它具有 电压高 能量密度大 自放电小 循环寿命长 无污染 无记忆效应等优点 可以适应不同范 围多层次绿色能源的需要 催化裂解甲烷制备的碳纳米管是由多层具有类石墨片状结构的同心 等径及中空圆锥形的 面叠合而成 类石墨层面取向与管轴倾斜[1,2] 这种特殊的微观结构使得锂离子的嵌入深度小 过程短 有大量的嵌锂空间 而且碳纳米管的高空隙率为有机溶剂分子的迁移提供了自由空间 使电极在大电流下充放电情况下极化程度小 可逆容量高 循环寿命长 甲烷催化裂解制备的 碳纳米管这种优异结构使得它非常有希望成为新一代锂离子电池的负极材料 本文研究了碳纳 米管制备温度对其嵌锂性能的影响 1 实验 1.1 碳纳米管的制备