应力幅值对Al-Zn-Mg合金微动疲劳损伤行为的影响.pdfVIP

Rare Metal Materials and Engineering Volume 41, Suppl. 2, September 2012 Cite this article as: Rare Metal Materials and Engineering, 2012, 41(S2): 136-140. Effect of Stress Amplitude on Fretting Fatigue Damage Behavior of Al-Zn-Mg Alloy Jiang Xiaosong, He Guoqiu, Liu Bing, Liu Xiaoshan Shanghai Key Lab. of DA for Metallic Functional Materials, Tongji University, Shanghai 200092, China Abstract: Effect of stress amplitude on fretting fatigue damage behavior of Al-Zn-Mg alloy was studied. Fretting fatigue tests were designed to determine the influence of stress amplitudes on fretting fatigue lives and fretting fatigue damage characteristics. Based on the macroscopic and microscopic experimental results of fretting fatigue of Al-Zn-Mg alloy, fretting fatigue characteristic and damage mechanism of Al-Zn-Mg alloy were intensively analyzed. Results show that stress amplitude affects the fretting fatigue performance significantly. With stress amplitude increasing, fretting fatigue lives are reduced nonlinearly and of certain relationship with the displacement amplitudes. There are two failure mechanisms, i.e. fretting wear and crack initiation along with propagation at the fretting fatigue damage zone, which are in competition relationship with stress amplitudes changing. Fretting fatigue crack initiates at the edge of fretting fatigue zone and fretting can accelerate fretting fatigue crack initiation and propagation. Key words: stress amplitude; Al-Zn-Mg alloy; fretting fatigue; damage mechanism Al-Zn-Mg alloys are used for structural applications in the the damages produced by fretting and the fretting fatigue life, aerospace and automotive industry because they present