Studies on microstructure and properties of MoS2-Cu coated graphite-Ag matrix composites ABSTRACT MoS2-Cu coated graphite-Ag matrix composites(group A) and MoS2- graphite -Ag matrix composites(group B) were prepared by powder metallurgy in this thesis;the effect of MoS2 content and Cu coated graphite on microstructure and properties of MoS2-Cu coated graphite-Ag matrix composites were studied;the tribological properties with and without electric current of both group A and group B composites were tested using the costom tribometer;tribological properties under different electric current density of 2%MoS 2-Cu coated graphite-Ag matrix composite was tested at last.Microstructure and worn surface were observed by metallurgy scope and SEM.The results show that for group A composites,density, hardness and bending strength are improved and electric resistivity does not show considerable change with MoS2 increasing; Properties of group A composites mentioned above are superior to group B composites.With and without electric current, wear rate of group A composites are much lower than group B composites, while coefficient of friction are slightly higher than group B composites. With MoS2 increasing, coefficient of friction of MoS2-Cu coated graphite-Ag matrix composites increase slightly while wear rate decreases remarkably with and without electric current; coefficient of friction under electric current of both group A and group B composites are smaller than those without electric current.2%MoS 2-Cu coated graphite-Ag matrix composite has good lubrication and low wear rate when the current density is below 20A/cm2.But current density above 20A/cm2 obviously weaken its friction and wear property. Keywords:MoS2-Cu coated graphite-Ag matrix composites,Bending strength, Wear rate,Coefficient of friction 致谢 学生时光 转瞬即 逝。在这临近 毕业、即 将 步入职业 生涯的 日子 里，我要感 谢所有关 心、帮 助过 我的人。 感谢我的 导师许 少凡 老师。两年多 的研究 生时光中 ，许 老师不 仅在学习 上 孜孜不 倦的对 我进 行 指导， 在生活 上也 给 了我无 限的关 怀。 我 的学位 论文是在 许少凡 老师的 全程 指 导下完 成的。 选题