超(超)临界机组锅炉受热面高温硫腐蚀与磨损防护技术研究.pdfVIP

超（超）临界机组锅炉受热面高温硫腐蚀与磨 损防护技术研究 李太江，李巍，李勇，刘立营，王博 西安热工研究院有限公司，陕西省西安市兴庆路 136 号 710032 ； Study on the Protective Techniques for the Heating Face of Super-Ultra Critical Unit from High Temperature Sulfur Corrosion and Erosion LI Tai-jiang, LI Wei, LI Yong, LIU Li-ying, WANG Bo Xi’an Thermal Power Research Institute Co., Ltd., Xi’an, 710049, China; ABSTRACT: In view of the employed to deposit NiCr cermet situation of shutting down for coatings on 2Cr13 substrates. The repairing due to the leakage and tube anti-sulfur corrosion behavior of the cracking caused by severe high NiCr cermet coating and 2Cr13 temperature sulfur corrosion, substrate was studied in an solid-particle erosion and wear, high atmosphere with high sulfur content. velocity oxygen fuel (HVOF) was The anti-erosion behavior of the NiCr - 1 - cermet coating and 2Cr13 was also 比较了相同腐蚀环境下涂层与抗腐 蚀性能较高的 2Cr13 基体的高温硫 studied. The results indicated that the 腐 蚀性能，同 时比较 了该涂层与 sealed NiCr cermet coating deposited 2Cr13 基体钢材的抗磨损性能。研究 by HVOF can reduce the high 结果表明超音速火焰喷涂的 NiCr 金 属陶瓷涂层具有比 2Cr13 钢更优的 temperature corrosion and erosion rate. 抗高温硫腐蚀性能。同时其抗高温 The 8000 hours in-field application of 磨损性能优于 2Cr13 钢。该超音速火 the NiCr cermet coating shows its 焰喷涂 NiCr 金属陶瓷涂层在贵州某 燃用高硫煤的电厂中经 8000 小时现 effectivity to protect the heating 场挂片考核后，涂层表面完好，可有 surface tube in super-ultra critical unit