含铝钛硅锰合金制备方法及粉化机理研究冶金工程专业论文.docxVIP

重庆大学硕士学位论文英 重庆大学硕士学位论文 英文摘要 PAGE PAGE IV macro-structure. So the directional solidification can be used to reduce alloy’s casting defects. ⑤ The alloy phase has been analyzed by EDS, XRD. The results show that the alloy phase TiFeSi2, β-Mn, AlFe3 and TiC exist in alloy. The viewpoint about Al3C4, AlP hydrolysis in wet environment causes the pulverization of alloy has been negated by the existence of TiC phase. The theory that the interaction between Al2O3 phase and matrix phase β-Mn causes residual stress to lead the Pulverization of the alloy has been put forward in this paper. Key word: Al-Mn-Si-Ti alloy, Pulverization, Crack source, Burning loss. 重庆大学硕士学位论文目录 重庆大学硕士学位论文 目 录 目 录 中文摘要I 英文摘要 II HYPERLINK \l _bookmark0 1 绪论 1 HYPERLINK \l _bookmark1 1.1 课题研究背景 1 HYPERLINK \l _bookmark2 1.1.1 世界锰产业形势分析 1 HYPERLINK \l _bookmark3 1.1.2 国内外研究现状 3 HYPERLINK \l _bookmark4 1.2 现阶段主要存在的问题 7 HYPERLINK \l _bookmark5 1.2.1 合金元素烧损 7 HYPERLINK \l _bookmark6 1.2.2 合金的粉化 8 HYPERLINK \l _bookmark7 1.3 课题研究目的及意义 9 HYPERLINK \l _bookmark8 2 实验 10 HYPERLINK \l _bookmark9 2.1 实验原料 10 HYPERLINK \l _bookmark10 2.2 实验设备 11 HYPERLINK \l _bookmark11 2.3 实验方案设计 13 HYPERLINK \l _bookmark12 2.3.1 探索最佳的铝块尺寸实验 15 HYPERLINK \l _bookmark13 2.3.2 减少铝烧损及防止合金粉化实验 18 HYPERLINK \l _bookmark14 2.4 合金的冶炼 21 HYPERLINK \l _bookmark15 2.4.1 温度控制 21 HYPERLINK \l _bookmark16 2.4.2 熔炼时间控制 22 HYPERLINK \l _bookmark17 2.4.3 凝固制度 22 HYPERLINK \l _bookmark18 3 实验结果及分析 23 HYPERLINK \l _bookmark19 3.1 合金元素烧损 23 HYPERLINK \l _bookmark20 3.1.1 铝的块度的确定 24 HYPERLINK \l _bookmark21 3.1.2 减少铝烧损的措施 30 HYPERLINK \l _bookmark22 3.2 粉化情况分析 33 HYPERLINK \l _bookmark23 3.2.1 合金元素的影响 35 HYPERLINK \l _bookmark24 3.2.2 炉渣碱度的影响 36 HYPERLINK \l _bookmark25 3.2.3 合金粉化的宏观分析 39 HYPERLINK \l _bookmark26 3.2.4 粉化合金与未粉化合金微观结构对比 40 HYPERLINK \l _bookmark27 3.2.5 粉化合金与未粉化合金物相分析 42 HYPERLINK \l _bookmark28 3.2.6 合金粉化诱导区域 Al2O3 夹杂的来源 47 HYPERLINK \l _bookmark29 3.2.7 合金的粉化机理